|a Estudio comparativo de la bioactividad de dos materiales biocerámicos =
|b Comparative study of the bioactivityof two bioceramic materials /
|c Margarita Trujillo Hernández, Rebeca E. Flores-Ventura, Angélica Suárez Porras, Leandro García González, Julián Hernández Torres [y otros dos].
|
| 246 |
3 |
1 |
|i Título paralelo
|a Comparative study of the bioactivityof two bioceramic materials
|
| 300 |
|
|
|a 1 recurso en línea (páginas 73-81) :
|b 1 ilustración a color, gráficos a color, archivo de texto, PDF.
|
| 500 |
|
|
|a En revista Odóvtos, vol. 21, no. 2 (mayo-agosto 2019)
|
| 500 |
|
|
|a Descripción basada en el contenido visto 20 de agosto, 2024
|
| 520 |
3 |
|
|a Los materiales a base de silicato de calcio han demostrado ser bioactivos debido a su capacidad para producir apatita carbonatada biológicamente compatible. El objetivo de este estudio fue analizar la bioactividad de Biodentine™ y MTA Repair HP® en contacto con discos de dentina humana, que se obturaron y dividieron aleatoriamente para formar cuatro grupos: grupo 1 Biodentine™, grupo 2 MTA Repair HP®, grupo control positivo MTA Angelus® y grupo control negativo IRM®, los cuales se incubaron en solución PBS durante 10 días, para posterior análisis por medio de MEB-EDS y Espectroscopía Raman. Los tres materiales a base de silicato de calcio analizados en este estudio demostraron ser bioactivos pues al entrar en contacto con una solución a base de fosfato desencadenaron la precipitación inicial de fosfato de calcio amorfo, que actúa como precursor durante la formación de apatita carbonatada.
|
| 520 |
3 |
|
|a Calcium silicate-based materials have been shown to be bioactive due to their ability to produce biologically compatible carbonated apatite. The objective of this study was to analyze the bioactivity of Biodentine ™ and MTA Repair HP® in contact with human dentine discs, which were sealed and divided randomly to form four groups: group 1 Biodentine™, group 2 MTA Repair HP®, positive control group MTA Angelus® and negative control group IRM®, which were incubated in PBS solution for 10 days, for a subsequent analysis by means of MEB-EDS and Raman spectroscopy. The three calcium-based materials analyzed in this study proved to be bioactive because upon contact with a phosphate-based solution they were triggered at the onset of amorphous calcium phosphate, as the precursor during the formation of carbonated apatite.
|
| 530 |
|
|
|a También disponible en formato HTML y EPUB
|
| 700 |
1 |
|
|a Flores Ventura, Rebeca E.
|e Autor/a
|
| 700 |
1 |
|
|a Suárez Porras, Angélica
|e Autor/a
|
| 700 |
1 |
|
|a García González, Leandro
|e Autor/a
|
| 700 |
1 |
|
|a Hernández Torres, Julián
|e Autor/a
|
| 856 |
4 |
1 |
|u https://revistas.ucr.ac.cr/index.php/Odontos/article/view/37061/37643
|y Ver artículo en línea
|
| 916 |
|
|
|a Centro Catalográfico
|
| 949 |
|
|
|a -JTG
|